Transition metal compositions

ABSTRACT

A transition metal composition which is the product of reacting a transition metal complex of empirical formula

United States Patent [191 Morris et al.

[ 1 June 11, 1974 22 Filed:

[ TRANSITION METAL COMPOSITIONS [76] Inventors: Arthur Morris; Hugh Thomas, both of Runcom, England [73 ""A's'sigfia' fnperfi lfiiniical Industries Tin? ited, London, England Mar. 20, 1972 [21] Appl. No.: 236,198

[30] Foreign Application Priority Data UNITED STATES PATENTS 1 3,326,877 6/1967 Orzechowski ct a1 252/431 R X 3,392,160 7/1968 Orzechowski 252/429 R X 3,424,777 1/1969 Wilke 252/431 R X 3,536,740 10/1970 Wilke 252/43] R X Primary Examiner-Patrick P. Garvin Attorney, Agent, or Firm-Cushman, Darby & Cushman [57] ABSTRACT A transition metal composition which is the product of reacting a transition metal complex of empirical formula with a substantially inert matrix material having a hydroxylic surface which is free from adsorbed water, wherein M is a metal of Group VllA of the Periodic Table, R is a hydrocarbon group or substituted hydrocarbon group, X is a monovalent ligand, and m and p are integers, m having a value from 2 up to the highest valence of the metal M and p having a value from 0 up to 2 less than the valence of the metal M The compositions are useful heterogeneous catalysts, for example for reforming of petroleum hydrocarbons or as olefin disproportionation catalysts. I

1 TRANSITION METAL COMPOSITIONS This invention relates to the disproportionation of olefins, and also to transition metal compositions suitable as initiators for use in such a process in which a transition metal complex is chemically bonded to a substantially inert matrix material.

It is known that organometallic compounds can be absorbed on inert inorganic materials and the resultant combination used as a heterogenous catalyst. However, the inorganic material serves merely as a support and does not affect the activity of the resultant catalyst.

We have discovered that certain organometallic complexes may be chemically bonded to inorganic matrices, to produce catalytically active compositions which may be of greater activity than the unmodified organometallic complex.

French Pat. No. 7,029,758 describes and claims a transition metal composition which is the product of reacting a transition metal complex of the general formula RmMx,

with a substantially inert matrix material having a hydroxylic surface which is free from adsorbed water, wherein M is a transition metal of Groups IVA to VIA of the Periodic Table of the Elements, R is a hydrocarbon group or substituted hydrocarbon group, X is a monovalent ligand, and m and p are integers, m having a value from 2 to the highest valency of the metal M and p having a value from to 2 less than the valency of the metal M, except when M is a metal of Group VIA when p is always 0.

(All references to the Periodic Table are to the version of the Periodic Table of the Elements printed inside the back cover of Advanced Inorganic Chemistry" by F.A. Cotton and G. Wilkinson, 2nd Edition, (1966), lnterscience Publishers, New York, London and Sydney).

According to one aspect of the present invention we now provide a transition metal composition which is the product of reacting a transition metal complex of empirical formula I R M'X with a substantially inert matrix material having a hydroxylic surface (as hereinafter defined) which is free from adsorbed water, wherein M is a metal of Group VIlA of the Periodic Table, R is a hydrocarbon group or substituted hydrocarbon group, X is a monovalent ligand, and m and p are integers, m having a value from 2 upto the highest valence of the metal M and p having a value from 0 upto 2 less than the valency of the metal M.

Many transition metal complexes exist as dimeric or other oligomeric species, and it is to be understood that such species are equally included within formula (1) above.

The transition metal is preferably rhenium; and the monovalent ligand X is preferably an anionic ligand, for example halogen. Hydrocarbon groups of different types may be associated with a single metal atom.

Suitable hydrocarbon groups R include alkyl and alkenyl groups (including rr-alkenyl groups such as rr-allyl) and substituted derivatives thereof. A preferred class of organic transition metal complexes are those in which some or all of the groups R are groups of general formula CH Y cr-bonded to the transition metal through the carbon atom. In this general formula Y may represent an atom or group capable of interaction with the vacant dorbitals of the metal M. Preferably allof the groups R have this formula, but it is possible for some of them to comprise other hydrocarbon groups.

Suitable substituent groups Y include aromatic and polyaromatic groups, for example, phenyl and naphthyl, giving rise, in formula (2) above, to the aralkyl ligands benzyl and (l-methylene-l-naphthyl) and ring substituted derivatives thereof, for example pmethylbenzyl.

Y may also be a cycloalkenyl group, for example, a cyclooctenyl group.

Alternatively, Y may comprise a group of general formula where Z represents carbon, silicon, germanium, tin or lead, and each R, which may be the same or different represents a hydrocarbon group or hydrogen; but is preferably an alkyl group. Suitable substituent groups Y thus include neopentyl and trimethylsilylmethyl; (CH3 and )3SICHg".

By a hydroxylic surface we mean a plurality of OH groups attached to the surface of the matrix material, the hydrogen atom of the OH group being capable of acting as a proton source, that is, having an acidic function. Such a material will be substantially inert in that, whereas the said OH groups are capable of reacting with, say, the transition metal hydrocarbyl complex, the bulk of the matrix material is chemically inert. Particularly good examples of such matrix materials are silica and alumina or mixtures thereof. These comprise a matrix of silicon or aluminium and oxygen atoms, to the surface of which OH groups are attached, the hydrogen atoms of said groups having an acidic function. However, apart from the presence of these OH groups, silica and alumina are generally regarded as chemically inert. Within the terms silica and alumina we include silicaand aluminabased materials containing small amounts of other suitable inorganic oxides, such as magnesium oxide and zinc oxide.

It is essential that the matrix material is freed from adsorbed water, as this would merely react with and destroy the transition metal complex. The matrix materials may be readily freed from such adsorbed water by, for example, a simple thermal treatment.

The reaction between the transition metal complex and matrix material comprises displacement of one or more of the hydrocarbon groups by the hydrogen atom of an OH group or groups, with liberation of the corresponding free hydrocarbon. The reaction may be represented by the following equation:'

wherein M, R, X, m and p have the meanings previously ascribed to them and n is an integer being not more than (m-l It has been found that when the defined components of our transition metal compositions are reacted, all except one of the hydrocarbon groups of the organometallic compound may be displaced by -OH groups of the matrix, so that there is always at least one hydrocarbon group attached to the transition metal in the product. This appears to be independent of the number of reactable hydroxylic groups present on the surface of the matrix.

The term Matrix (-OH),, represents an inert matrix having at least it reactable hydroxylic groups attached to its surface. The number of reactable hydroxylic groups, that is, the number available for reaction, will depend on the nature and condition of the matrix material. For example, in some materials, because of their molecular configuration, some of the hydroxylic groups present are not reactive under our conditions. Thus, it is usual to characterise a sample of the matrix material before use, for example, by reaction with an excess of the transition metal complex or as described below.

The progress of the reaction in the manner indicated in equation (4) above may be readily followed by the evolution of free hydrocarbon RH or by colour changes in the reactants. The fact that the product is a chemical entity, not a physical mixture such as a transition metal complex physically adsorbed on a granular matrix, may be demonstrated by removing the product, a coloured, insoluble composition, from the reactants and washing it with a solvent which would remove any adsorbed complex from the matrix. When this is done, the complex remains on the matrix. Contrary to this, when our complexes are mixed with an inert matrix containing no reactable hydroxylic groups, for example silica which has been calcined at l,200 C, although the complex is adsorbed on the matrix, it is readily removed by washing the product with a solvent.

As previously mentioned, the number of reactable hydroxylic groups present in a given weight of matrix will depend upon its nature (for example, whether it is silica or alumina) and its condition (for example, its surface area and the treatment it has received to remove adsorbed water). Thus the precise composition of transition metal compositions according to our invention may vary from one batch or sample to another of the same matrix material; but successive portions of the same material prepared under identical conditions will give products having the same composition.

Compositions according to the present invention may be prepared by contacting a solution of the transition metal complex with a suitable matrix material, in the absence of free or adsorbed water. The solvent used for the complex should be dry and inert; hydrocarbon solvents are preferred. Since many of the transition metal complexes which may be used in our process are thermally unstable, the reaction temperature must be maintained low enough to avoid decomposition of the complex. With some complexes, temperatures below C are required. Depending on the air-sensitivity of the transition metal complex it may also be necessary to operate in oxygemfree conditions, for example, under a nitrogen blanket.

The ratio of transition metal complex to matrix material may be varied within wide limits depending upon the physical and chemical nature of the components used; but it is preferred that the proportions and the nature of the reacting materials, for example, the values of m and p, are so chosen that at least two and preferably at least three hydrocarbon groups remain attached to the transition metal atom in the product composition. Preferably, substantially all the hydroxylic groups of the matrix material are reacted with the transition metal complex.

The matrix material may be characterised in a number of ways. A first method comprises suspending the matrix material, which has previously been freed from water, in an inert liquid, and titrating the reactable hydroxylic groups with a solution of the transition metal complex in an inert solvent. Since most transition metal complexes are strongly coloured, the end-point is readily detectable by the presence of a permanent colouration in the suspending solvent. In compositions prepared in this way, all the reactable hydroxylic groups of the matrix are reacted with the metal complex. The compositions produced may then be recovered by filtration from the reaction medium, freed from solvent and stored dry or under solvent in oxygen-free conditions.

It is possible, if desired, to add less than the complete titre of transition metal complex, or even to add excess transition metal complex, but when excess complex is used, it will remain in the reaction medium when the composition is separated.

A second method for preparing compositions according to our invention comprises, first, characterising a sample of the material by adding excess of an organometallic transition metal complex (which may or may not have the formula (1) above) or a Grignard reagent (magnesium hydrocarbyl halide) to a sample of the matrix material and determining the number of molecules of hydrocarbon liberated from a known amount of matrix material; and secondly, adding to a further portion of the matrix material just sufficient of the desired transition metal complex to liberate an appropriate amount of hydrocarbon. For example, a sample of the matrix material may be suspended in a solvent and excess of a transition metal 'rr-allylic compound added. The volume of propylene produced is measured and related to the weight of matrix material. A second sample of the matrix material is then taken and the appropriate transition metal i-r-allylic complex added until the volume of propylene produced per gram of matrix material present is equivalent to that previously determined by addition of excess transition metal complex.

As already mentioned, the compositions may be separated from the media in which they are produced and exist as chemical entities of definite composition. In many cases they are more thermally stable than the transition metal complexes from which they are produced.

Compositions prepared as described above may have useful catalytic activity. For example, rheniumcontaining compositions may be used as reforming catalysts for petroleum hydrocarbon.

According to another aspect of the present invention, we provide a process for the disproportionation of olefinically unsaturated hydrocarbons in which the olefinically unsaturated hydrocarbon is contacted with an initiator which is the product of reacting a transition metal complex of empirical formula R MX with a substantially inert matrix material having a hydroxylic surface which is free from adsorbed water, wherein M is molybdenum, tungsten or rhenium, R is a hydrocarbon group or a substituted hydrocarbon group, X is a monovalent ligand and m and p are integers, m having a value from 2 upto the highest valence of the metal M and p having a value from 0 up to 2 less than the valence of the metal M.

As described above, the monovalent ligand X is preferably an anionic ligand, for example halogen, and the groups R may be the same or different.

Suitable hydrocarbon groups R include alkyl and alkenyl groups (including 'rr-alkenyl groups such as 1r-allyl) and substituted derivatives thereof. A preferred class of organic transition metal complexes are those in which some or all of the groups R are groups of general formula -CH Y o-bonded to the transition metal through the carbon atom. In this general formula Y may represent an atom or group capable of interaction with the vacant dorbitals of the metal M. Preferably all of the groups R have this formula, but it is possible for some of them to comprise other hydrocarbon groups.

Suitable substituent groups Y include aromatic and polyaromatic groups, for example, phenyl and naphthyl, giving rise, in formula (2 above, to the aralkyl ligands benzyl and (l-methylene-l-naphthyl) and ring substituted derivatives thereof, for example pmethylbenzyl.

Y may also be a cycloalkenyl group, for example, a cyclooctenyl group.

Alternatively, Y may comprise a group of general formula where Z represents carbon, silicon, germanium, tin or lead, and each R, which may be the same or different,

Particularly when molybdenum and rhenium complexes of formula (5) above are employed in the production of the initiator, it is preferred that the transition metal complex is an oligomeric, for example dimeric species, as in tetrakis(1r-allyl)dimolybdenum or hexakis(1r-allyl)dirhenium.

It is also preferred that the values of m and p are such that at least three groups R remain attached to the metal atom M in the initiator composition.

Conveniently, the initiator is employed in a finely divided form, e.g., particles, granules, pellets or the like.

Since the transition metal complexes are often airor water-sensitive, it is preferred to operate under anhydrous and oxygen-free conditions, for example by drying all solvents used in the preparation of the initiator or in the disproportionation reaction and by operating under an oxygen-free atmosphere, for example nitrogen or the reactant gases.

By disproportionation is meant a reaction between two olefinically unsaturated molecules with cleavage of the double bonds and recombination of the resultant fragments to form different olefinically unsaturated materials.

Such a reaction commonly gives more than one product, but in all cases the sum of the number of carbon atoms of the products equals the sum of the number of carbon atoms of the reactants.

Disproportionation may occur between two molecules of the same material, when two products are normally produced, one of higher molecular weight than the starting material and one of lower molecular weight. For example, butene can give a mixture of C C olefins and hexene a mixture of C -C olefins. Alternatively, molecules of two different materials may react, as for example, in the reaction of but-l-ene and pent-Z-ene to give propylene and hex-3-ene.

The term olefinically unsaturated hydrocarbon is intended to include both mono-olefins, for example ethylene, propylene, butenes, pentenes and hexenes, and polyenes, for example butadiene.

Alternatively, cyclic olefins, for example cyclopentene or norbomene (bicyclo [2.2.1]hept-2-ene) may be employed as starting material. Disproportionation in such a case involves ring opening at the olefmic double bond and recombination of the resultant fragments. This process may occur repetitively to produce polymeric materials; for example disproportionation of cyclopentene produces a linear, rubbery polypentenamer.

The reaction is carried out by contacting the olefinically unsaturated hydrocarbon with the initiator.

The starting materials may be 'liquid or gaseous under the conditions of reaction. The starting materials may be dissolved in a suitable inert solvent or diluent, for example a parafi'mic hydrocarbon, but it is preferred to operate in the absence of solvent.

The reaction may be carried out as a batch process in a suitable vessel, preferably with agitation of the contents to ensure intimate contact of the reactants and the initiator.

Alternatively, the reactants may be caused to flow past the initiator. The reactants may be caused to percolate through a fixed bed of initiator, or the initiator particles may be suspended in a moving stream of the reactants, Preferably, the initiator particles are caused to flow in countercurrent fashion to the moving stream of reactants.

Alternatively, the initiator may be employed as a fluidised bed. Preferably, a gaseous reactant is used to induce fluidisation of the initiator particles.

Temperature and pressure of reaction are not critical. It is preferred to operate at ambient pressure, but particularly with gaseous reactants, higher pressures may be employed. The temperature of reaction will depend on the desired reaction rate, but it is to be noted that higher temperatures commonly favour the production of products of higher carbon number. It will be appreciated that isomerisation of starting material or initial products may occur as determined by the thermodynamics of the system, and this tendency may be increased by increased contact times over the catalyst.

On completion of reaction, materials may be separated from the catalyst by conventional means, for example decantation or filtration. If desired, individual reaction products may be separated from each other or from unreacted starting materials, for example by distillation.

Particularly when the initiator is employed in a liquid suspension, it may be desirable to increase the surface area of the initiator composition by subjecting it to a comminution procedure, for example by subjecting a suspension of the initiator to ultrasonic dispersion.

The invention is now illustrated by the following Examples. In all the Examples, transition metal complexes and compositions containing them were prepared and handled under an atomosphere of dry, oxygen-free nitrogen or, where appropriate, were blanketed with the olefin undergoing reaction. All solvents and diluents were dried by distillation from sodium wire, and were deoxygenated before use. The products of disproportionation reactions were analyzed by gas-liquid chromatography.

PREPARATION OF TRANSITION METAL COMPLEXES Example 1 Preparation of molybdenum allyl Molybdenum pentachloride was dissolved in diethyl ether, and equivalents of a ethereal solution of allylmagnesium chloride were added dropwise at ambient temperature, while the mixture was stirred vigorously.

On completion of reaction, the deep green solution was filtered to remove magnesium chloride, and the ether was stripped off in vacuo. The residue was extracted with the minimum quantity of dry, deoxygenated pentane to give a deep green solution which was shown by infra-red spectroscopy to contain tetrakis(1rallyl) molybdenum and the dimeric species tetrakis(rrallyl)dimolybdenum. For reasons of convenience, this mixture will be referred to as molybdenum allyl.

The tetrakis(1r -allyl) molybdenum could be purified, if required, by fractional crystallisation.

Example 2 Preparation of tetrakis(1r-allyl) molybdenum An ethereal solution of molybdenum pentachloride was added dropwise over a period of 3 hours to a stirred solution of allyl magnesium chloride in tetrahydrofuran at 60 C until the molar ratio of molybdenum pentachloride to Grignard reagent was 0.18:]. The mixture was evaporated to dryness in vacuo and the residue was extracted with pentane at ambient temperature to give a yellow solution. This solution was concentrated, and held at -40 C overnight when yellow crystals of tetrakis(1r-allyl)molybdenum separated out. These were purified by sublimation at 60-65 C and l torr pressure, and identified by infra-red spectroscopy.

Example 3 Preparation tetrakis(1rallyl)dimolybdenum Tetrakis(1r-allyl)dimolybdenum (molybdenum ir-allyl dimer) was prepared according to the method described and claimed in our copending British Pat. Application No. 30266/71.

Dimolybdenum tetra-acetate was suspended in dry, degassed, diethyl ether in the proportion of 200 mmole per litre. The suspension was blanketed with nitrogen and 900 mmole of allyl magnesium chloride were added per litre of suspension, as a 0.45 M solution in diethyl ether. The mixture was stirred at ambient temperature for about 1.5-2.5 hours until all the solid material had dissolved and the solution was a dark green colour.

The solution was evaporated to dryness and the resultant green residue was extracted four times with pentane to give a pale green solution of tetrakis(1rallyl)dimolybdenum, which was identified by infra-red spectroscopy.

Example 4 Preparation of tetrakis(1r-crotyl) dimolybdenum Tetrakis(1r-crotyl)dimolybdenum was prepared by the method described and claimed in our copending British Patent Application No. 30266/71.

Dimolybdenum tetra-acetate .was suspended in dry, deoxygenated diethyl ether in the proportion of 311 mmole per litre.

The suspension was added dropwise over a period of 1 hour to a stirred ethereal solution of crotyl magnesium bromide at 0 C, until the molar ratio of dimolybdenum tetra-acetate to Grignard reagent was 1:5 .36.

Stirring was continued until all the dimolybdenum tetra-acetate had dissolved, and the resultant green solution was evaporated to dryness. The residue was extracted with dry, deoxygenated pentane at 40 C to give a dark green solution which is believed to be tetrakis(1r-crotyl)dimolybdenum.

Example 5 Preparation of tetrakis('n'-allyl) tungsten Solid tungsten hexachloride was added over a period of 2 hours to a stirred solution of lithium allyl in diethyl ether/tetrahydrofuran at ambient temperature, until the molar ratio of tungsten hexachloride to lithium allyl was 1:8. The resultant brown mixture was stirred for another hour and the solvents were removed in vacuo at ambient temperature.

The brown residue was extracted with pentane at -40 C to give a pale brown solution from which pale brown crystals of tetrakis(1r-allyl)tungsten could be recovered. These were purified by sublimation at 75 C and a pressure of l torr, and identified by infra-red spectroscopy.

Example 6 Preparation of rhenium rr-allyl Anhydrous rhenium pentachloride was dissolved in pure, anhydrous diethyl ether to give an orange-red solution.

The solution was cooled to 70 C and 5 equivalents of an ethereal solution of allylmagnesium chloride were added while the reaction mixture was stirred.

Example 7 Preparation of bis(allyl)rhenium chloride An .ethereal suspension of rhenium pentachloride was added dropwise over a period of 2 hours to a stirred solution of lithium allyl in tetrahydrofuran at 60 C until the molar ratio rhenium pentachloride to lithium allyl was 1:7. The brown mixture was stirred for another hour and the solvents were removed in vacuo.

The brown residue was extracted with pentane to yeild a brown solution. This was evaporated to dryness, and the resultant solid product sublimed at 75 C and a pressure of 0.1 torr to give a yellow oil.

A mass spectrum of this oil gave a parent ion at m/e 302, with a Re, C1 isotope pattern indicative of bis- (allyl )rhenium chloride.

Example 8 Preparation allyl)dirhenium Hexakis(1r-allyl)dirhenium (rhenium 1r-allyl dimer) was prepared according to the method described and claimed in our copending British Pat. Application No. 30266/71.

Dichloro-dirheniumtetra-acetate was suspended in dry diethyl ether in the proportion of 50 mmole per litre. The reaction vessel was purged with nitrogen, and 350 mmole of allyl magnesium chloride per litre of suspension were added slowly, as a 0.14 M solution in diethyl ether. The contents of the reaction vessel were stirred during addition of the allyl magnesium chloride. The yellow-orange suspension was immediately converted to a deep redbrown solution.

After 1 hour at ambient temperature, the reaction mixture was evaporated to dryness while holding the temperature below C. The solid residue was extracted three times with dry, deoxygenated pentane, at a temperature below 0 C, to give a deep red-brown solution of hexakis(1r-allyl)dirhenium, which was identified by infra-red spectroscopy and mass spectral analysis. This solution was stored under nitrogen at a temperature below 40 C.

Preparation of Initiator Compositions In the following Examples, the appropriate matrix material was dried in vacuo torr) as described in the Examples and was then cooled under dry nitrogen. The dry material was suspended in the minimum quantity of dry, deoxygenated pentane and the suspension titrated with a pentane solution of the appropriate transition metal complex, prepared as in Examples 1-8, until a pennanent colouration remained in the suspending solvent. The coated composition was recovered by filtration, washed with pentane and dried in vacuo.

Alternatively, the initiator could be employed as a suspension in pentane.

Example 9 Molybdenum allyl/alumina with butl-ene 60-80 mesh BSS 'y-alumina (Koninklijke Zwavelzuurfabrieken v/h Ketjen N.V. Grade Ck 300) was dried at 500 C for 12 hours and reacted with molybdenum allyl.

of hexakis(1r- The product, which was coloured brown and contained 1.8 percent by weight of molybdenum, was placed in a dry flow reactor in an atmosphere of dry, oxygen-free nitrogen. But-l-ene, which had been deoxygenated and dried by passing it over freshly prepared, supported copper turnings (BTS Catalyst) and molecular sieve (type 5A) was passed through the catalyst bed at 25 C for 12 hours, at a velocity'calculated to give a contact time of 12 seconds.

The effluent gas contained C -C olefins, the average butene conversion being 2 percent.

Conversion could be temporarily increased to 6 per cent by increasing the reactor temperature to C.

Progressive increases in reactor temperature temporarily increased catalyst activity, and also altered the product distribution towards the higher carbon numbers.

At 200 C, product olefins ranged from C to C and, also, substantial isomerisation to but-2-ene was occurring.

Example 10 Molybdenum allyl/silica with hexl-ene Silica (Manosil Grade VN3) was dried at 500 C for 12 hours and reacted with molybdenum allyl.

The coated silica, which contained 0.077 percent by weight of molybdenum, was packed in a column, and 15 times its weight of hex-l-ene vapour, at reflux temperature, was passed through the column over a period of 4 hours.

Apart from butene, the effluent contained decene (46 percent), nonene 12 percent), octene (2 percent), heptene (13 percent), and unreacted hex-l-ene (27 percent).

Example 11 Molybdenum allyl/alumina with norbornene 'y-Alumina (Grade CK 300) was dried at 500 C for 24 hours and was reacted with molybdenum allyl. The product contained 0.32 percent by weight of molybdenum.

The initiator was mixed with five times its weight of norbornene and the mixture was heated to C for 2 hours. I

The initiator was removed by filtration, and methanol added to the filtrate to precipitate a rubbery polymer.

Evaporation of the solvents after precipitation of the polymer left a sweet-smelling yellow oil, which was shown by analysis to be a mixture of oligomers of norbornene.

Example 12 Tetrakis(1r-allyl)molybdenum/silica gel with hex-l-ene Silica gel (Davison Chemical Co. Grade 952) was dried at 650 C for 12 hours and was reacted with tetrakis(rr-allyl)molybdenum. The product was yellowbrown, and contained 1.1 percent by weight of molybdenum.

Hex-l-ene was added to the initiator, in the proportion of 20 dm per kg, and'the mixture was stirred at ambient temperature for 20 hours.

At the end of this time, 67 percent of the hexene had reacted; 35 percent to decene and ethylene, 18 percent to heptene and pentene, 11 percent to nonene and propylene, and 3 percent to octene and butene. Example 13 Tetrakis(1r-allyl)molybdenum/silica gel with hexl-ene The procedure of Example 12 was repeated, except the silica gel was dried at 200 C for 12 hours. The

coated silica gel was brown and contained 1.5 percent by. weight of molybdenum.

After 1 hour reaction at 60 C, 20 percent of the hexene had been converted almost exclusively to decene and ethylene.

Example 14 Molybdenum rr-allyl dimer/alumina with hex-l-ene 'y-Alumina (Grade CK 300) was dried at 500 C for 12 hours and reacted with molybdenum rr-allyl dimer.

The product, which was coloured black and contained 2.4 percent by weight of molybdenum, was placed in a round-bottomed flask, together with five times its own weight of hex-l-ene. Ethylene was evolved on contact of the hexene with the catalyst composition at ambient temperature.

The flask contents were heated to 35 C for 4 hours. At the end of this period, analysis of the flask contents showed that 25 percent of the hexene had been converted to ethylene and decene.

Exemple l5 Molybdenum rr-allyl dimer/alumina with hex-l-ene The procedure of Example 14 was repeated at a temperature of 35 C for 24 hours followed by a period of 4 hours at reflux temperature.

The conversion of hex-l-ene to ethylene and decene was 75 percent. In addition, about percent of the product olefins were derived from isomers of hexl-ene.

Example 16 Molybdenum vr-allyl dimer/alumina with hex-l-ene 'y-Alumina pellets (Grade CK 300) were dried at 500 C and reacted with molybdenum.1r-allyl dimer. The alumina turned dark brown. The coated alumina was mixed at ambient temperature with dry, degassed hex-l-ene (7.5 dm of hexene per kg. of alumina).

After 4 hours at ambient temperature, 76 percent of the hexene was converted to ethylene and dec-5-ene. The mixture was warmed to 80 C when further reaction occurred. The liquid became viscous and gasliquid chromatography showed the presence of C -C hydrocarbons.

Example 17 Molybdenum rr-allyl dimer/silica gel with hex-l-ene Silica gel (Grade 952) was dried at 650 C for 12 hours and reacted with tetrakis(11-allyl)dimolybdenum. The product was a very dark green black and contained 3 percent by weight of molybdenum.

Hex-l-ene was added to the initiator, in the proportion of 20 dm per kg, and the mixture was stirred at 60 C for 4 hours.

20 percent of the hexene was converted almost exclusively to decene and ethylene.

Example 18 Molybdenum 1r-al1yl dimer/silica gel with 'hexl -ene The procedure of Example 17 was repeated, except that the silica gel was dried at 200 C. The coated silica gel was deep maroon and contained 3.5 percent by weight of molybdenum.

After hours reaction at 60 C, 35 percent of the hexene was converted almost-exclusively into decene and ethylene.

Example 19 Molybdenum rr-allyl dimer/alumina with hept-3-ene y-Alumina was dried at 500 C and reacted with molybdenum rr-allyl dimer. The product was dark brownblack and contained 2.3 percent by weight of molybdenum.

Hept-3-ene was added to the initiator, in the proportion of 10 dm per kg, and the mixture was allowed to stand at ambient temperature for 18 hours.

14 percent of the heptene reacted; 10 percent to decenes and butenes, 3 percent to octenes and hexenes, and 1 percent nonenes and pentenes.

Example 20 Molybdenum ir-allyl dimer/alumina with 3,3-dimethylbutene-l y-Alumina was dried at 500 C and reacted with molybdenum 'rr-allyl dimer. The product was dark brownblack and contained 2.3 percent by weight of molybdenum.

3,3-Dimethylbutene-l was added to the initiator, in the proportion of 10 dm per kg, and the mixture was allowed to stand at ambient temperature for 24 hours.

16 percent of the dimethylbutene was converted to a mixture of C olefins.

Example 21 Molybdenum 1r-allyl dimer/alumina with cyclopentene rr-Alumina (Grade CK 300) was dried at 500 C for 24 hours and was coated with molybdenum 'n-allyl dimer. The product contained 2.4 percent by weight of molybdenum.

The initiator was charged to a stainless steel autoclave, together with cyclopentene, in a weight ratio of 4.6135. The mixture was stirred at ambient temperature and autogenous pressure for 5 hours and was then allowed to stand for 2 days.

The resultant clear, viscous liquid was washed from the initiator with benzene and was evaporated to dryness to yield a rubber-like polymer. This was shown by infra-red spectroscopy to be a polypentenamer (-(CI T CH;CH CH CHH-m with (is and trans forms in the ratio of 47:53.

The conversion of cyclopentene to polymer was 12 percent.

Example 22 crotyl)dimolybdenum/alumina with hexl -ene 'y-Alumina pellets were dried at 500 C and reacted with tetrakis (ir-crotyl)dimolybdenum. The product was a dark chocolate-brown and contained 1.3 percent by weight of molybdenum.

The initiator was mixed with hex-l-ene (10 drn of hexene/3 kg of alumina)'and the mixture was stirred at 20 C for 2 hours. At this end of this period 6.5 percent of the hexene had reacted; 4.2 percent to decenes and ethylene, 1.3 percent to nonenes and propylene, and the remainder to octenes,-heptenes, pentenes and butenes.

Example 23 Tetrakis(1r-allyl)tungsten/alumina with hex-l-ene 'y-Alumina (Grade CK 300) was dried at 500 C for 12 hours and reacted with tetrakis(1r-allyl) tungsten. The product contained 0.8 percent by weight of tungsten.

The initiator was placed in a round-bottomed flask, together with hex-l-ene, in a weight ratio of 3: 10. Evolution of ethylene occurred on contact of the hexene with the catalyst composition at ambient temperature.

The flask contents were heated to 35 C for 8 hours. At the end of this period, the conversion of hex-l-ene to ethylene and decene was 25 percent.

Tetrakis(7r- 13 Example 24 Tetrakis(1r-allyl )tungsten/alumina with hex-l-ene The procedure of Example 23 was repeated at a temperature of 35 C for 24 hours, followed by a period of 6 hours at reflux temperature.

Conversion of hex-l-ene to ethylene and decene was 70 percent. In addition, about percent of the product olefins were derived from isomers of hex-l-ene. Example 25 Rhenium rr-allyl/alumina with hexl-ene 'y-Alumina (Grade CK 300) was dried at 500 C for 1 hour and reacted with rhenium vr-allyl. The product was a pale brown.

Hex-l-ene was refluxed with the initiator for several hours to give dec-S-ene.

Example 26 Bis(allyl)rhenium chloride/alumina with hex-l-ene 'y-Alumina was dried at 500 C and reacted with bis- (allyl) rhenium chloride. The product was pale brown and contained 5 percent by weight of rhenium.

Hex-l-ene was added to the initiator at ambient temperature, in the proportion of 4 drn per kg. A vigorous evolution of ethylene occurred immediately.

After 2 hours reaction at ambient temperature, 57 percent of the hexene was converted almost exclusively to decene and ethylene.

Example 27 Bis(allyl)rhenium chloride/alumina with cyclopentene 'y-Alumina was dried at 500 C and was reacted with bis(allyl) rhenium chloride. The product was pale brown and contained 5 percent by weight of rhenium.

A solution of cyclopentene in toluene (5.66M) was stirred with the initiator for 24 hours at ambient temperature, in the proportion of drn per kg.

5 percent of the cyclopentene was converted to a yellow elastomeric material. Example 28 Rhenium 1r-allyl dimer/alumina with hex-l-ene 'y-Alumina was dried at 500 C for 3 hours and was reacted with rhenium rr-allyl dimer. The product was brown.

The initiator was mixed at ambient temperature with dry degassed hex-l-ene (4 drn of hexene per kg of alumina). immediate evolution of ethylene occurred.

After 2 hours reaction, 14 percent of the hexene was converted to dec-S-ene.

What we claim is:

1. A process for the production of transition metal compositions in which a solution or suspension of a transition metal complex of empirical formula R MX,

is reacted with a substantially inert matrix material having a hydroxylic surface which is free from adsorbed water, wherein M is a metal of Group VIIA of the Periodic Table, R is a hydrocarbon group or substituted alkyl group of formula -CH Y where Y is a group of formula Z(R') where Z is silicon, germanium, tin or lead and each R is a hydrocarbon group or hydrogen, X is halogen, and m and p are integers, m having a value from 2 up to the highest valence of the metal M and p having a value from 0 up to 2 less than the valence of the metal M under dry and oxygen-free conditions.

2. A process as claimed in claim 1 in which the groups R are rr-allyl, benzyl, p-methylbenzyl, l-methylene-l-naphthyl, neopentyl or trimethylsilylmethyl.

3. A process as claimed in claim 1 in which the metal M is rhenium.

4. A process as claimed in claim 3 in which the transition metal complex is hexakis(1r-allyl)dirhenium or bis- (allyl)rhenium monhalide.

5. A process as claimed in claim 1 in which the matrix material is silica or alumina.

6. A process as claimed in claim 1 in which the proportions of transition metal complex and the matrix material are so chosen that substantially all the reactable hydroxylic groups of the matrix are reacted with the transition metal complex.

7. A process as claimed in claim 6 in which a suspen sion of the matrix material which has been freed from adsorbed water, is titrated with a solution of the transition metal complex.

8. A process as claimed in claim 6 in which, prior to reaction with the transition metal complex, a sample of the matrix material has been characterised by adding to the sample a solution of a hydrocarbyl transition metal complex or a Grignard reagent and measuring the amount of hydrocarbon liberated.

9. A transition metal composition which is the product of reacting a transition metal complex of empirical formula with a substantially inert matrix material having a hydroxylic surface which is free from adsorbed water, wherein M is a metal of Group VIIA of the Periodic Table, R is a hydrocarbon group or substituted hydrocarbon group of the formula -Cl-I Y where Y is a group of formula Z(R') where Z is silicon, germanium, tin or lead and each R is a hydrocarbon group or hydrogen, X is halogen, and m and p are integers, m having a value from 2 up to the highest valence of the metal M and p having a value from 0 up to 2 less than the valence of the metal M. 

2. A process as claimed in claim 1 in which the groups R are pi -allyl, benzyl, p-methylbenzyl, 1-methylene-1-naphthyl, neopentyl or trimethylsilylmethyl.
 3. A process as claimed in claim 1 in which the metal M1 is rhenium.
 4. A process as claimed in claim 3 in which the transition metal complex is hexakis( pi -allyl)dirhenium or bis(allyl)rhenium monhalide.
 5. A process as claimed in claim 1 in which the matrix material is silica or alumina.
 6. A process as claimed in claim 1 in which the proportions of transition metal complex and the matrix material are so chosen that substantially all the reactable hydroxylic groups of the matrix are reacted with the transition metal complex.
 7. A process as claimed in claim 6 in which a suspension of the matrix material which has been freed from adsorbed water, is titrated with a solution of the transition metal complex.
 8. A process as claimed in claim 6 in which, prior to reaction with the transition metal complex, a sample of the matrix material has been characterised by adding to the sample a solution of a hydrocarbyl transition metal complex or a Grignard reagent and measuring the amount of hydrocarbon liberated.
 9. A transition metal composition which is the product of reacting a transition metal complex of empirical formula RmM1Xp with a substantially inert matrix material having a hydroxylic surface which is free from adsorbed water, wherein M1 is a metal of Group VIIA of the Periodic Table, R is a hydrocarbon group or substituted hydrocarbon group of the formula -CH2Y where Y is a group of formula Z''(R'')3 where Z is silicon, germanium, tin or lead and each R'' is a hydrocarbon group or hydrogen, X is halogen, and m and p are integers, m having a value from 2 up to the highest valence of the metal M1 and p having a value from 0 up to 2 less than the valence of the metal M1. 